Kinetics of borided gear steels
(Springer, 2013)In this study, the case properties and diffusion kinetics of GS18NiMoCr36 (GS18), GS22NiMoCr56 (GS22) and GS32NiCrMo6.4 (GS32) gear steels borided in Ekabor-II powder were investigated by conducting a series of experiments ... -
Kinetics of plasma paste boronized AISI 8620 steel in borax paste mixtures
(Springer, 2013)In the present study, AISI 8620 steel was plasma paste boronized by using various borax paste mix tures. The plasma paste boronizing process was carried out in a dc plasma system at a temperature of 973, 1023 and 1073 K ... -
Plasma paste boronizing of AISI 8620, 52100 and 440C steels
(Elsevier, 2011)In the present study, AISI 8620, 52100 and 440C steels were plasma paste boronized (PPB) by using 100% borax paste. PPB process was carried out in a dc plasma system at temperature of 700 and 800 °C for 3 and 5 h in a gas ... -
Surface characterization of pack and plasma paste boronized of 21NiCrMo2 steel [Kutu ve plazma pasta borlanmiş 21NiCrMo2 çeliǧinin yüzey karekterizasyonu]
(Journal of the Faculty of Engineering and Architecture of Gazi University, 2012)In the present study, 21NiCrMo2 steel were plasma paste boronized by using 100 wt.% B2O3, 70 wt.% B2O3 + 30 wt. % SiC, 70 wt.% B2O3 + 30 wt.% B4C, 30 wt. % B2O3 + 70 wt.% SiC, 30 wt.% B2O3 + 70 wt.% B4C pastes. This steel ... -
Wear and corrosion behaviour of borided and nitrided m2 high speed steel
(Journal of the Balkan Tribological Association, 2013)Boriding and nitriding lead to improved tribological and corrosive properties of M2 high speed steel. Boronising treatment was carried out in Ekabor-II powders at the process temperature of 950 degrees C for 4 h. Gas ... -
Wear behaviour of plasma paste boronized of AISI 8620 steel with borax and B2O3 paste mixtures
(Elsevier, 2013)In the present study, AISI 8620 steel was plasma paste boronized (PPB) by using paste mixtures with different borax and B2O3 percentages. The PPB process was carried out in a DC plasma system at 973, 1023 and 1073 K for 5 ...