Effects of CO2 and H2S on corrosion of martensitic steels in brines at low temperature
Künye
R. Feng, J. Beck, D. M. Hall, A. Buyuksagis, M. Zıomek-Moroz And S.N. Lvov, “ Effects Of Co2 And H2s On Corrosion Of Martensitic Steels İn Brines At Low Temperature”, Corrosion, March 2018, Vol. 74, No. 3, Pp. 276-287, Doi = 10.5006/2406.Özet
Corrosion studies were conducted for martensitic carbon steels in 5 wt% NaCl brine solutions at 4°C and 10 MPa (1,450 psi). These studies simulated different subsurface environments relevant to Arctic drilling. Here, two high-strength martensitic carbon steels, S-135 and UD-165, were studied in three different environments: (1) a CO2-NaCl-H2O solution with a CO2:H2O molar ratio of 0.312 in the whole system, (2) an H2SNaCl- H2O solution with an H2S:H2O molar ratio of 3.12 × 10−4, and (3) a CO2-H2S-NaCl-H2O solution with the same acid gas to water ratios as environments 1 and 2. Results from the CO2+H2S mixed environment indicated that sour corrosion mechanism was dominant when the CO2:H2S molar ratio was 1,000. This impact of a small amount of H2S on the corrosion mechanism could be attributed to the specific adsorption of H2S on the steel surface. Electrochemical and mass loss measurements showed a distinct drop in the corrosion rate (CR) by more than one order of magnitude when transitioning from sweet to sour corrosion. This inhibiting effect on CR was attributed to the formation of a protective sulfide thin film.
Kaynak
CorrosionCilt
74Sayı
3Koleksiyonlar
- Makaleler [31]
- Scopus İndeksli Yayınlar Koleksiyonu [137]
İlgili Öğeler
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
-
Effects of CO2 and H2S on corrosion of martensitic steels in NaCl(aq) at low temperature
Feng, R.; Beck, Justin; Hall, D.M.; Büyüksağiş, Aysel; Ziomek-Moroz, M.; Lvov, S.N. (Nace International, 2016)Corrosion studies were conducted for martensitic carbon steels in brine solutions at 4 °C and 10 MPa (1450 psi), which simulated the subsurface environments encountered in Arctic drilling. Three environments with a 5 % wt. ... -
Corrosion of 13Cr steel at the Cement/Casing interface in CO2/H2S environments at 4, 85 and 200 °C
Beck, Justin; Feng, R.; Hall, D.M.; Büyüksağiş, Aysel; Lvov, S.N.; Ziomek-Moroz, M. (Nace International, 2018)A study was carried out to investigate corrosion at the cement/casing interface for 13Cr casing steel. Cement simulated pore solution (CSPS) was developed by exposing cement pieces to 5% NaCl at 100 °C and 10 MPa in ... -
Effects of H2S and CO2 on Cement/Casing interface corrosion integrity for cold climate oil and gas well applications
Beck, Justin; Feng, R.; Hall, D.M.; Büyüksağiş, Aysel; Ziomek-Moroz, M.; Lvov, S.N. (The Electrochemical Society, 2016)Low-temperature corrosion relevant to oil and gas wells was investigated. Casing cement was exposed to brine in contact with CO2 at 4 °C and 10 MPa. Pore water was extracted from wet cement using a die press, and a cement ...