Gd2O3 ve La2O3 katkılı atık ambalaj camının radyasyon zırhlama uygulamalarında kullanılabilirliğinin araştırılması

Abstract

In this study, the usability of soda-lime-sand glass added separately with two different oxides as Gd2O3 and La2O3 in radiation shielding applications was investigated. Both additives were added separately at 0.005 %, 0.05 % and 0.5 % by weight and the melting process was achieved by providing homogeneous mixture. Then, density, molar volume and linear attenuation coefficient measurements were carried out. As a result, the density value of 2.8033 g/cm3 and linear attenuation coefficient value of 8.11 cm-1 were obtained with 0.5 % Gd2O3 addition and therefore the usability of waste packaging glass in low energy radiation shielding applications was observed.

Bu çalışmada, Gd2O3 ve La2O3 olarak iki farklı oksitle ayrı ayrı katkılandırılmış atık ambalaj camının radyasyon zırhlama özellikleri üzerine kullanılabilirliği araştırılmıştır. Her iki katkı % 0.005, % 0.05 ve % 0.5 kütlece oranlarında ayrı ayrı eklenmiş ve homojen karışım sağlanarak ergitme süreci gerçekleştirilmiştir. Daha sonra yoğunluk, molar hacim ve doğrusal zayıflama katsayısı ölçümleri yapılmıştır. Sonuç olarak, 2.8033 g/cm3 yoğunluk değeri ve 8.11 cm-1 doğrusal zayıflatma katsayısı değeri % 0.5 katkılı Gd2O3 cam kompozisyonu ile elde edilerek atık ambalaj camının düşük enerjili radyasyon zırhlama uygulamalarında kullanılabilirliği görülmüştür.