Diffusion bonding of AZ91 using a silver interlayer
(Nisan 2008)
Diffusion bonding of AZ91 alloy with a silver interlayer was carried out at 480C for different times under
1 MPa in a vacuum of 2x10^-3Pa. Shear test was applied to measure the shear strengths of the joints in
the room ...
An investigation on renewable energy education at the university level in Turkey
(2011)
In the present study, to discover how teaching of renewable energy sources in Turkey is carried out at the
university level, a questionnaire was developed and applied at different universities in Turkey. The
analyses ...
Problems and solution offers related to the vocational and technical orientation in Turkey
(Şubat 2015)
When we look at the process during which the need for manpower in the sectors related to production, decreased and a system
based on automation, was implemented along with the use of technology in the production; the ...
Investigation of diffusion kinetics of plasma paste borided AISI 8620 steel using a mixture of B2O3 paste and B4C/SiC
(Springer, 2013)
In the present study, AISI 8620 steel was plasma paste borided by using
various B2O3 paste mixture. The plasma paste boriding process was carried out in a
dc plasma system at temperatures of 973, 1023 and 1073 K for 2, ...
Plasma paste boronizing of AISI 8620, 52100 and 440C steels
(Elsevier, 2011)
In the present study, AISI 8620, 52100 and 440C steels were plasma paste boronized (PPB) by using 100% borax paste. PPB process was carried out in a dc plasma system at temperature of 700 and 800 °C for 3 and 5 h in a gas ...
Kinetics of borided gear steels
(Springer, 2013)
In this study, the case properties and diffusion kinetics of
GS18NiMoCr36 (GS18), GS22NiMoCr56 (GS22) and GS32NiCrMo6.4 (GS32) gear
steels borided in Ekabor-II powder were investigated by conducting a series of experiments ...
Diffusion bonding of electroless Ni plated WC composite to Cu and AISI 316 stainless steel
(2011)
In this study, a composite containing WC (Tungsten Carbide) and Ni was produced by two different processing routes. Electroless Ni coated WC powders were consolidated and sintered at 1200 ◦C. Diffusion bonding couples of ...
Investigation of corrosion behavior of borided gear steels
(Springer, 2014)
In this study, corrosion behaviors of GS18NiMoCr36 (GS 18) and GS32NiCrMo6.4 (GS 32) gear steels borided in Ekabor-II powder at the temperature of 950 °C for 2 and 6 h were investigated in a 6 % M HCI acid solution. The ...
Wear behaviour of plasma paste boronized of AISI 8620 steel with borax and B2O3 paste mixtures
(Elsevier, 2013)
In the present study, AISI 8620 steel was plasma paste boronized (PPB) by using paste mixtures with different borax and B2O3 percentages. The PPB process was carried out in a DC plasma system at 973, 1023 and 1073 K for 5 ...
Investigation of surface properties and wear resistance of borided steels with different B4C mixtures
(Niscair, 2012)
Boriding is a thermo-chemical surface hardening treatment applied to iron based materials. This treatment is performed by boron element diffusing into iron based materials at high temperatures. Wear resistance increases ...