The examination of corrosion behaviors of HAP coated Ti implant materials and 316L SS by Sol-Gel method 1
(Pleiades Publishing, Ltd, 2011)
In this research, hydroxyapatite (HAP) coatings have been produced on Ti, Ti6Al4V alloy and 316L stainless steel substrates by sol–gel method. (NH4) H2PO4 is taken as P precursor and Ca(NO3)2 4H2O is taken as Ca precursor ...
Corrosion behaviors of hydroxyapatite coated by electrodeposition method of Ti6Al4V, Ti and AISI 316L SS substrates
(Pleiades Publishing, Ltd, 2013)
Electrodeposition method was used to obtain hydroxyapatite (HAP) coatings on Ti6Al4V, Ti and AISI 316L SS substrates. Electrodeposition solution is prepared as Ca(NO3)2 ⋅ 4H2O and (NH4)H2PO4. Additionally, three different ...
Electrochemical corrosion of Ti6Al4V, Ti and AISI 316L SS after immersed in concentrated simulated body fluid
(Pleiades Publishing, Ltd, 2016)
The biomimetic method is used to obtain hydroxyapatite (HAP) coatings on Ti6Al4V, Ti and AISI 316L SS substrates. These substrates with different pretreatment surface operations (HNO3, anodic polarization, base-acid) were ...
Corrosion behaviours of hydroxyapatite coated by biometic method of Ti6Al4V, Ti and AISI 316L SS substrates
(ACADEMIA ROMÂNĂ, 2012)
Biomimetic method was used to obtain hydroxyapatite (HAP) coatings on Ti6Al4V, Ti and AISI 316L SS substrates. The solutions were prepared as 1.5xSBF and 3.0xSBF similarly to body fluid (SBF). Additionally, three different ...