The examination of corrosion behaviors of HAP coated Ti implant materials and 316L SS by Sol-Gel method 1
(Pleiades Publishing, Ltd, 2011)
In this research, hydroxyapatite (HAP) coatings have been produced on Ti, Ti6Al4V alloy and 316L stainless steel substrates by sol–gel method. (NH4) H2PO4 is taken as P precursor and Ca(NO3)2 4H2O is taken as Ca precursor ...
The coating of hydroxyapatite ( HAP ) on 316L stainless steel and Ti6Al4V alloy use by Sol-Gel method
(Afyon Kocatepe Üniversitesi, 2010)
In this research, hydroxyapatite (HAP) coatings have been coated on Ti6Al4V alloy and 316 L stainless steel substrates by sol-jel method. (NH4)H2PO4 is taken as P precursor and Ca(NO3)2.4H2O is taken as Ca precursor to ...
Corrosion and wear behaviors of boronized AISI 316L stainless steel
(Springer, 2013)
In this study, the effects of a boronizing treatment on the corrosion and wear behaviors of AISI 316L austenitic stainless steel (AISI 316L) were examined. The corrosion behavior of the boronized samples was studied via ...
Corrosion behaviors of hydroxyapatite coated by electrodeposition method of Ti6Al4V, Ti and AISI 316L SS substrates
(Pleiades Publishing, Ltd, 2013)
Electrodeposition method was used to obtain hydroxyapatite (HAP) coatings on Ti6Al4V, Ti and AISI 316L SS substrates. Electrodeposition solution is prepared as Ca(NO3)2 ⋅ 4H2O and (NH4)H2PO4. Additionally, three different ...
Corrosion behaviours of hydroxyapatite coated by biometic method of Ti6Al4V, Ti and AISI 316L SS substrates
(ACADEMIA ROMÂNĂ, 2012)
Biomimetic method was used to obtain hydroxyapatite (HAP) coatings on Ti6Al4V, Ti and AISI 316L SS substrates. The solutions were prepared as 1.5xSBF and 3.0xSBF similarly to body fluid (SBF). Additionally, three different ...