Borlanmış sementasyon çeliğinin tribolojik özelliklerinin incelenmesi
(El-Cezerî Fen ve Mühendislik Dergisi, 2019)
Bu çalışmada farklı B2O3/SiC/B4C pasta karışımlarında plazma pasta borlanmış sementasyon çeliğinin yüksek yük altındaki aşınma davranışları inceleniştir. Plazma borlama işlemi vakum altında 10 mbar işlem basıncında, H2 ve ...
Corrosion and wear behaviors of boronized AISI 316L stainless steel
(Springer, 2013)
In this study, the effects of a boronizing treatment on the corrosion and wear behaviors of AISI 316L austenitic stainless steel (AISI 316L) were examined. The corrosion behavior of the boronized samples was studied via ...
Investigation of corrosion and wear behavior of borided AISI P20 steel in micro-wave furnace
(IOP Publishing, 2019)
In this study, the effect of microwave boronizing treatment on the corrosion and wear behaviour of boride layer formed on AISI P20 steel have been investigated. The boronizing treatment was carried out using Ekabor-II ...
Wear and corrosion behaviour of borided and nitrided m2 high speed steel
(Journal of the Balkan Tribological Association, 2013)
Boriding and nitriding lead to improved tribological and corrosive properties of M2 high speed steel. Boronising treatment was carried out in Ekabor-II powders at the process temperature of 950 degrees C for 4 h. Gas ...
Adhesion and wear properties of boro-tempered ductile iron
(Elsevier, 2011)
In this study, adhesion and wear properties of boro-tempered ductile iron (BDI) were investigated. Boro-tempering was carried out on two stage processes i.e. boronizing and tempering. At the first stage, ductile iron samples ...
Wear behaviour of plasma paste boronized of AISI 8620 steel with borax and B2O3 paste mixtures
(Elsevier, 2013)
In the present study, AISI 8620 steel was plasma paste boronized (PPB) by using paste mixtures with different borax and B2O3 percentages. The PPB process was carried out in a DC plasma system at 973, 1023 and 1073 K for 5 ...
Investigation of tribological behaviour of plasma paste boronized of AISI 8620, 52100 and 440C steels
(Niscair, 2011)
In the present study, AISI 8620, 52100 and 440C steels were plasma paste boronized (PPB) by using 100% borax paste. PPB process was carried out in a dc plasma system at temperature of 700 and 800 °C for 3 and 5 h in a gas ...
Analysis with taguchi method of wear behaviors of borided AISI 52100 steels
(Journal of The Balkan Tribological Association, 2013)
In this study, case properties and analysis of wear behaviour of borided AISI 52100 steel with the Taguchi method were investigated by conducting a series of experiments in Ekabor-II powders at process temperatures of 850, ...