Corrosion behaviours of hydroxyapatite coated by biometic method of Ti6Al4V, Ti and AISI 316L SS substrates
(ACADEMIA ROMÂNĂ, 2012)
Biomimetic method was used to obtain hydroxyapatite (HAP) coatings on Ti6Al4V, Ti and AISI 316L SS substrates. The solutions were prepared as 1.5xSBF and 3.0xSBF similarly to body fluid (SBF). Additionally, three different ...
Corrosion behavior of 13Cr casing steel in cement-synthetic pore solution exposed to high pressure CO2 and H2S
(The Electrochemical Society, 2015)
The electrochemical corrosion behavior of grade L-80, type 13Cr casing steel was investigated in cement-synthetic pore solution (CSPS) exposed to CO2 and H2S using in-situ electrochemical methods and ex-situ surface analyses ...
The use of papaver somniferum L. Plant extract as corrosion inhibitor
(Pleiades Publishing, Ltd, 2019)
The corrosion inhibition and adsorption characteristics of the extract obtained from the plant Papaver somniferum L. (PSL) by electrochemical methods at different temperatures (25, 35 and 45°C) were investigated in 0.2 M ...
Tertiary amine methacrylate based polymers as Corrosion Inhibitors in double distilled water. Part I
(Pleiades Publishing, Ltd, 2019)
In the current study, the inhibitive performances of tertiary amine methacrlate based water soluble diblock copolymers on the corrosion behaviour of AISI 304 stainless steel were investigated in double distilled water (DDW, ...
Tertiary amine methacrylate based polymers as corrosion ınhibitors in hcl solution. Part II
(Pleiades Publishing, Ltd, 2019)
In this study, the inhibitive performance of novel synthesised water-soluble of different molecular weight diblock copolymers of derivative methyl methacrylate (VB84, VB206, VB207, VB361, VB371,VB406) on the corrosion ...
Wear and corrosion behaviour of borided and nitrided m2 high speed steel
(Journal of the Balkan Tribological Association, 2013)
Boriding and nitriding lead to improved tribological and corrosive properties of M2 high speed steel. Boronising treatment was carried out in Ekabor-II powders at the process temperature of 950 degrees C for 4 h. Gas ...