Hydroxyapatite (HAP) coating with biomimetic method abstract
(Afyon Kocatepe Üniversitesi, 2009)
Biomimetik yöntemle hidroksiapatit (HAP) kaplama en gelecek vaat eden tekniklerden birisidir. Bu çalışmada, üç farklı ön yüzey işlemi (HNO3, anodik polarizasyon, 5 N NaOH-1 N HCl (BA)) altlıkların (Ti ve Ti6Al4V) yüzey ...
Effects of CO2 and H2S on corrosion of martensitic steels in NaCl(aq) at low temperature
(Nace International, 2016)
Corrosion studies were conducted for martensitic carbon steels in brine solutions at 4 °C and 10 MPa (1450 psi), which simulated the subsurface environments encountered in Arctic drilling. Three environments with a 5 % wt. ...
The effect of alcohol on the passivation of Al alloys in 1 N H 2 SO 4 solution
(Pleiades Publishing, Ltd, 2010)
In this study, the influence of different alcohol on the passivation of aluminium alloys have been investigated by using current potential curves. Experimental results show that the addition of alcohol in H2SO4 solution ...
Tertiary amine methacrylate based polymers as corrosion ınhibitors in hcl solution. Part II
(Pleiades Publishing, Ltd, 2019)
In this study, the inhibitive performance of novel synthesised water-soluble of different molecular weight diblock copolymers of derivative methyl methacrylate (VB84, VB206, VB207, VB361, VB371,VB406) on the corrosion ...
The effect of 3-Methyl 1-Pentyn 3-ol on the corrosion of Al-Si-Cu alloys in acid solutions by using SEM, EDX and AAS
(Pleiades Publishing, Ltd, 2009)
In this study, the effect of alloying elements on the corrosion of Al-Si-Cu alloys in H 2 SO 4 and HCl media content 3-methyl–1pentyn–3-ol (3mlp3ol) is investigated by using SEM, EDX, AAS. The effect of active elements and ...
Corrosion behaviors of hydroxyapatite coated by electrodeposition method of Ti6Al4V, Ti and AISI 316L SS substrates
(Pleiades Publishing, Ltd, 2013)
Electrodeposition method was used to obtain hydroxyapatite (HAP) coatings on Ti6Al4V, Ti and AISI 316L SS substrates. Electrodeposition solution is prepared as Ca(NO3)2 ⋅ 4H2O and (NH4)H2PO4. Additionally, three different ...
Effects of H2S and CO2 on Cement/Casing interface corrosion integrity for cold climate oil and gas well applications
(The Electrochemical Society, 2016)
Low-temperature corrosion relevant to oil and gas wells was investigated. Casing cement was exposed to brine in contact with CO2 at 4 °C and 10 MPa. Pore water was extracted from wet cement using a die press, and a cement ...
Investigation of Corrosion Behaviours Hydroxyapatite (HAP) coated Ti6Al4V Implants by Using Electrochemical Deposition Method
(2018)
In this research, hydroxyapatite (HAP) has been coated on the Ti6A14V alloy surface by electrophoresis
method. In this electrophoresis method, NH4H2PO4 is taken as P precursor and Ca (NO3)2.4H2O is taken
as Ca precursor ...
The effect of polypyrrole and nickel + polypyrrole coatings on corrosion behaviour AISI 304 stainless steel
(Pleiades Publishing, Ltd, 2015)
Polypyrrole (PPy) and nickel + PPy (Ni + PPy) coatings have been occured on AISI 304 stainless steel (304 SS) surface by cyclic voltammetry technique in aqueous oxalic acid solutions and as the supporting electrolytes was ...
Corrosion of 13Cr steel at the Cement/Casing interface in CO2/H2S environments at 4, 85 and 200 °C
(Nace International, 2018)
A study was carried out to investigate corrosion at the cement/casing interface for 13Cr casing steel. Cement simulated pore solution (CSPS) was developed by exposing cement pieces to 5% NaCl at 100 °C and 10 MPa in ...