dc.contributor.authorYıldız, İsmail
dc.contributor.authorGüneş, İbrahim
dc.contributor.authorUygunoğlu, Tayfun
dc.contributor.authorAslantaş, Kubilay
dc.contributor.authorEvcin, Atilla
dc.contributor.authorÇelik, A. Gürhan
dc.contributor.authorPehlivan, Melikhan
dc.contributor.authorMavi, Tuğçe
dc.contributor.authorKatip, Cem Tolga
dc.date.accessioned2019-12-19T13:15:50Z
dc.date.available2019-12-19T13:15:50Z
dc.date.issued28.04.2019en_US
dc.identifier.urihttps://www.researchgate.net/publication/334250233_Sol-Jel_Yontemiyle_Borlanmis_Inconel_Alasiminin_Yuzey_Karakterizasyonu
dc.identifier.urihttps://hdl.handle.net/11630/7521
dc.description.abstractBu çalışmada, Inconel alaşımı sol-jel mettodu kullanılarak borlanmıştır. Borlama sonrası numuneler elektrik rezistanslı fırında 900○C'de 1 saat bekeltilerek sinterlemiştir. Numuneler kesitten kesilerek gerekli metolografik işlemlerden geçilirek numunelerin borür tabaka kalınlıkları Nikon MA100 marka optik mikroskop yardımıyla ölçülmüştür. Borlanmış numunelede oluşan fazların analizi Shimadzu XRD-6000 model X-ışınları cihazı yardımıyla tespit edilmiştir. Borlama işlemi sonucunda Inconel 625 alaşımında NiB, Ni2B, Ni3B, Ni4B3, MoB, CrB ve Cr2B fazları elde edilmiştir. Borlama sıcaklık ve süresine bağlı olarak 4.1-9.7 μm arasında borür tabakaları elde edilmiştir. Üç farklı bor bileşiğinde farklı mikro sertlik değerleri elde edilmiştir. Tinkal’de 1673 HV0.1, Sassolit’de 1997 HV0.1, B4C’de 2375 HV0.1, İşlemsiz Inconel 625 alaşımınında ise 541 HV0.1 sertlik değerleri elde edilmiştir.en_US
dc.description.abstractIn this study, surface characterization of boronized inconel alloy was investigated by sol gel method. The samples were sintered at 900ºC for 1 hour in a furnace with electrical resistance. The boride samples were cut from the section and the boride layer thicknesses obtained after the required sanding and polishing processes were measured with the help of Nikon MA100 optic microscope. Borate phases were obtained by using Shimadzu XRD 6000 brand XRD device and micro hardness tests were carried out with Shimadzu HMV-2 brand tester. As a result of XRD analysis of boron Inconel samples, NiB, Ni2B, Ni3B, Ni4B3, MoB, CrB and Cr2B phases were obtained. Depending on boron temperature and time, boron layers were obtained on Inconel samples with thicknesses ranging from 4.1-9.7 μm. The micro hardness values of the boronized Inconel samples were 541 HV0.1 in the untreated sample while the hardness values of tinkal 1673 HV0.1, Sassolit 1997 HV0.1 and boron carbide 2375 HV0.1 were obtained.en_US
dc.language.isoturen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectInconelen_US
dc.subjectSol-Jelen_US
dc.subjectBorlamaen_US
dc.subjectYüzey Karakterizasyonuen_US
dc.subjectInconelen_US
dc.subjectSol Gelen_US
dc.subjectBoronizingen_US
dc.subjectCharacterization.en_US
dc.titleSol-Jel yöntemiyle borlanmış inconel alaşımının yüzey karakterizasyonuen_US
dc.typeconferenceObjecten_US
dc.relation.journal4th International Conference on Engineering Technology and Applied Sciences (ICETAS)en_US
dc.departmentİscehisar Meslek Yüksekokuluen_US
dc.authorid0000-0002-9207-591Xen_US
dc.identifier.startpage248en_US
dc.identifier.endpage251en_US
dc.relation.publicationcategoryKonferans Öğesi - Uluslararası - Kurum Öğretim Elemanıen_US
dc.contributor.institutionauthorGüneş, İbrahim
dc.contributor.institutionauthorUygunoğlu, Tayfun
dc.contributor.institutionauthorAslantaş, Kubilay
dc.contributor.institutionauthorEvcin, Atilla


Bu öğenin dosyaları:

Thumbnail

Bu öğe aşağıdaki koleksiyon(lar)da görünmektedir.

Basit öğe kaydını göster