Utilization of different waste glasses to fabricate foamed glasses
Üst veriTüm öğe kaydını göster
Waste management strategies have an essential role for more sustainable environment as well as for circular economy model. With this motivation, foamed glasses are one of the key candidate for achieving waste utilization purposes. The present paper is aimed at valorisation of different waste materials including flint container, green container, sodium-lamp, amber pharma and screen cover glasses by adding marble tailings (as a source of CaCO3) as foaming agent to fabricate foamed glass product. Each waste glasses obtained from municipal waste storage area was washed, crushed, milled and screened so as to prepare the batches composed of 97 % waste glasses and the remaining as marble tailings. The cylinderical samples with 26-mm Ø were obtained by applying uniaxial hydrolic pressing at 0.7 MPa and heating step was carried out at 900 °C by adjusting 10 °C/min heating rate, then followed by keeping at the peak temperature for 30 min. The fabrication of foamed glasses based on different glass wastes and marble tailings were successfully achieved, and the properties of bulk density, porosity, water absorption and compressive strength were measured. It was observed that waste glasses with marble tailings can be integrated to form a lightweight foamed glass with good mechanical properties.
KaynakInternational Symposium on Innovations in Civil Engineering and Technology Abstract Book
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
Fabrication of foamed glass by valorization of ferrochromium slags and flint container glass waste Kurtuluş, Recep; Kavas, Taner (International Symposium on Innovations in Civil Engineering and Technology, 16.12.2019)Ferrochromium processes generate a vast quantity of ferrochromium slags which are accumulated in landfills. Not only economical uselessness but also detrimental environmental effects occur due to the accumulation of these ...
In this study, a foam glass material was produced by using green container glass waste as main component, quartz mining tailings for compositional adjustment, marble powder as a source of CaCO3 for foaming agent and ...
Fotovoltaik panellerde kullanılan camlar, güneş hücrelerini çevresel etmenlere karşı korumanın yanı sıra, ışığı geçirebilme kabiliyetlerine göre panellerin çıkış gücü performansını doğrudan etkilerler. Bu nedenle güneş ...