The examination of corrosion behaviors of HAP coated Ti implant materials and 316L SS by Sol-Gel method 1
(Pleiades Publishing, Ltd, 2011)
In this research, hydroxyapatite (HAP) coatings have been produced on Ti, Ti6Al4V alloy and 316L stainless steel substrates by sol–gel method. (NH4) H2PO4 is taken as P precursor and Ca(NO3)2 4H2O is taken as Ca precursor ...
Corrosion and wear behaviors of boronized AISI 316L stainless steel
(Springer, 2013)
In this study, the effects of a boronizing treatment on the corrosion and wear behaviors of AISI 316L austenitic stainless steel (AISI 316L) were examined. The corrosion behavior of the boronized samples was studied via ...
Corrosion behaviors of hydroxyapatite coated by electrodeposition method of Ti6Al4V, Ti and AISI 316L SS substrates
(Pleiades Publishing, Ltd, 2013)
Electrodeposition method was used to obtain hydroxyapatite (HAP) coatings on Ti6Al4V, Ti and AISI 316L SS substrates. Electrodeposition solution is prepared as Ca(NO3)2 ⋅ 4H2O and (NH4)H2PO4. Additionally, three different ...
Investigation of electrochemical corrosion behavior in a 3.5wt.% NaCl solution of boronized dual-phase steel
(Elsevier, April 2013)
In this study, corrosion behaviors of boronized and non-boronized dual-phase steel were investigated
with Tafel extrapolation and linear polarization methods in a 3.5 wt.% NaCl solution. Microstructure analyses show that ...
Wear and corrosion behaviour of borided and nitrided m2 high speed steel
(Journal of the Balkan Tribological Association, 2013)
Boriding and nitriding lead to improved tribological and corrosive properties of M2 high speed steel. Boronising treatment was carried out in Ekabor-II powders at the process temperature of 950 degrees C for 4 h. Gas ...