dc.contributor.authorGür, Bahri
dc.contributor.authorAyhan, Muhammed Emre
dc.date.accessioned2021-08-02T07:28:14Z
dc.date.available2021-08-02T07:28:14Z
dc.date.issued24.02.2021en_US
dc.identifier.citationGür, B , Ayhan, M . (2021). Molibden Oksit, Pluronic®F127 ve Mantarın Lityum tetraborat/ITO Elektrotların Kapasitif Özelliklerine Etkilerinin İncelenmesi . Afyon Kocatepe Üniversitesi Fen ve Mühendislik Bilimleri Dergisi , 21 (1) , 196-208 . DOI: 10.35414/akufemubid.870456en_US
dc.identifier.urihttps://dergipark.org.tr/tr/pub/akufemubid/issue/60443/870456
dc.identifier.urihttps://doi.org/10.35414/akufemubid.870456
dc.identifier.urihttps://hdl.handle.net/11630/8973
dc.description.abstractGünümüzde alternatif enerji üretim süreçleri, üretilen enerjinin verimli bir şekilde depolanması ve enerji kaynaklarının çevre dostu malzemelerden üretilmesi önemli araştırma konularıdır. Bu amaçla enerji depolamada kullanılacak süper kapasitörlerde elektrot materyali olarak iletken polimerler, grafite alternatif mantar gibi biyokütle katkıları ve geçiş metal oksitleri (GMO) elektrokimyasal olarak araştırılmıştır. Elektrot hazırlarken lityum tetraborat (LTB) doping tuzu olarak tercih edilmiştir. LTB’ye sırasıyla molibden oksit (MoO3), Pluronic®F127 ve mantar katkılanarak elektrotlar hazırlanmıştır. Hazırlanan elektrotların elektrokimyasal özellikleri uygulanan potansiyel aralığındaki akım yoğunluğu değişimi dikkate alınarak araştırılmış ve elde edilen bulgular LTB-MoO3-F127-Mantar/ITO elektrotun daha iyi elektrokimyasal enerji depolama kapasitesine sahip olduğunu göstermiştir. Elektrokimyasal çalışmalarda LTB-MoO3-F127-Mantar/ITO elektrotta LTB/ITO elektrota kıyasla yaklaşık 3,5 kat kapasitif etkinin artırıldığı ve elektrot çevrim ömrünün 20 çevrim sonrası %86 (anodik) ve %87 (katodik) oranlarında korunduğu gösterilmiştir. Bu çalışma ile süper kapasitör uygulamaları için uygun maliyetli, yüksek performanslı ve çevre dostu teknoloji olarak grafite alternatif önerilen mantar-karbon tabanlı anot teknolojisi geliştirmek amacıyla GMO, iletken polimer ve mantar katkılamasının optimize edilerek grafit anotların yerini alabileceği önerilmiştir.en_US
dc.description.abstractNowadays, alternative energy production processes, efficient storage of generated energy, and the production of energy resources from environmentally friendly materials are important research topics. For this purpose, conductive polymers, biomass additives such as mushroom and transition metal oxides (GMO) as electrode materials were investigated electrochemically towards supercapacitors used in energy storage. While preparing the electrode, lithium tetraborate (LTB) was preferred as the doping salt. Electrodes were prepared by adding molybdenum oxide (MoO3), Pluronic®F127, and mushroom to LTB, respectively. The electrochemical properties of the prepared electrodes were investigated considering the current density variation in the applied potential range, and the findings obtained showed that LTB-MoO3-F127-Mushroom/ITO electrode increased capacitive effect approximately 3.5 times compared to LTB/ITO electrode, and electrode cycle life was preserved at 86% (anodic) and 87% (cathodic) rates after 20 cycles. In electrochemical studies, it has been shown that the capacitive effect of LTB-MoO3-F127-Mushroom/ITO electrode is increased approximately 3.5 times compared to LTB/ITO electrode and that the electrode cycle life is preserved at 86% (anodic) and 87% (cathodic) rates after 20 cycles. In this study, a low cost, high performance, and environmentally friendly alternative technology is presented for super capacitor applications. It has been shown that the developed mushroom-carbon-based anode technology can replace graphite anodes by optimizing GMO, conductive polymer, and mushroom doping.en_US
dc.language.isoturen_US
dc.publisherAfyon Kocatepe Üniversitesien_US
dc.identifier.doi10.35414/akufemubid.870456en_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectİnce Filmen_US
dc.subjectDöndürerek Kaplamaen_US
dc.subjectSüper Kapasitören_US
dc.subjectDöngüsel Voltametrien_US
dc.subjectİstiridye Mantarıen_US
dc.subjectPluronic®F127en_US
dc.subjectThin Filmen_US
dc.subjectSpin Coatingen_US
dc.subjectSuper Capacitoren_US
dc.subjectCyclic Voltammetryen_US
dc.subjectOyster Mushroomen_US
dc.subjectPluronic®F127en_US
dc.titleMolibden oksit, pluronic®F127 ve mantarın lityum tetraborat/ITO elektrotların kapasitif özelliklerine etkilerinin incelenmesien_US
dc.title.alternativeInvestigation of the effects of molybdenum oxide, pluronic®F127 and mushroom on capacitive properties of lithium tetraborate/ITO electrodesen_US
dc.typearticleen_US
dc.relation.journalAfyon Kocatepe Üniversitesi Fen ve Mühendislik Bilimleri Dergisien_US
dc.departmentAfyon Kocatepe Üniversitesien_US
dc.authorid0000-0003-0579-6354en_US
dc.authorid0000-0003-2324-6858en_US
dc.identifier.volume21en_US
dc.identifier.startpage196en_US
dc.identifier.endpage208en_US
dc.identifier.issue1en_US
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Başka Kurum Yazarıen_US


Bu öğenin dosyaları:

Thumbnail

Bu öğe aşağıdaki koleksiyon(lar)da görünmektedir.

Basit öğe kaydını göster