Investigation of corrosion behavior of borided gear steels

Abstract

In this study, corrosion behaviors of GS18NiMoCr36 (GS 18) and GS32NiCrMo6.4 (GS 32) gear steels borided in Ekabor-II powder at the temperature of 950 °C for 2 and 6 h were investigated in a 6 % M HCI acid solution. The boride layer was characterized by optical microscopy, X-ray diffraction technique and the Micro-Vickers hardness tester. X-ray diffraction analysis of boride layers on the surface of the steels revealed the existence of FeB, Fe2B, CrB and Cr2B compounds. The thickness of the boride layer increases by increasing boriding time for gear steels. The hardness of the boride compounds formed on the surface of the steels GS 18 and GS 32 ranged from 1,728 to 1,905 HV0,05 and 1,815 to 2,034 HV0,05 respectively, whereas Vickers hardness values of the untreated steels GS 18 and GS 32 were 335 HV0,05 and 411 HV0,05, respectively. The corrosion resistance of borided gear steels is higher compared with that of unborided steels. The boride layer increased the corrosion resistances of gear steels 4–6-fold.