Yayıncı "Nace International" için listeleme
Toplam kayıt 4, listelenen: 1-4
-
Corrosion behavior of ultra-high strength drilling steel in alkaline brines containing hydrogen sulfide at high temperature
(Nace International, 2016)In-situ electrochemical measurements were used to study the sour corrosion of ultra-high strength low alloy carbon steel (UHSLA) in alkaline brines at 200 °C. The solutions were buffered with NaHCO3 / Na2CO3 / NaOH to pH ... -
Corrosion of 13Cr steel at the Cement/Casing interface in CO2/H2S environments at 4, 85 and 200 °C
(Nace International, 2018)A study was carried out to investigate corrosion at the cement/casing interface for 13Cr casing steel. Cement simulated pore solution (CSPS) was developed by exposing cement pieces to 5% NaCl at 100 °C and 10 MPa in ... -
Effects of CO2 and H2S on corrosion of martensitic steels in brines at low temperature
(Nace International, 2018)Corrosion studies were conducted for martensitic carbon steels in 5 wt% NaCl brine solutions at 4°C and 10 MPa (1,450 psi). These studies simulated different subsurface environments relevant to Arctic drilling. Here, two ... -
Effects of CO2 and H2S on corrosion of martensitic steels in NaCl(aq) at low temperature
(Nace International, 2016)Corrosion studies were conducted for martensitic carbon steels in brine solutions at 4 °C and 10 MPa (1450 psi), which simulated the subsurface environments encountered in Arctic drilling. Three environments with a 5 % wt. ...