Corrosion behavior of 13Cr casing steel in cement-synthetic pore solution exposed to high pressure CO2 and H2S
(The Electrochemical Society, 2015)The electrochemical corrosion behavior of grade L-80, type 13Cr casing steel was investigated in cement-synthetic pore solution (CSPS) exposed to CO2 and H2S using in-situ electrochemical methods and ex-situ surface analyses ... -
Corrosion behavior of 13Cr casing steel in cement-synthetic pore solution exposed to high pressure CO2 and H2S
(The Electrochemical Society, 2015)As deeper wells drilled for oil and gas extraction encounter higher pressures, temperatures, and concentrations in the downhole environment, it becomes increasingly important to consider the integrity of the casing that ... -
Effect of H2S and CO2 on Cement/Casing alloy interface corrosion integrity for cold climate oil and gas well applications
(The Electrochemical Society, 2016)A study has been carried out to investigate sweet and sour corrosion at the cement-casing interface for offshore oil and gaswells in cold climate. The test solution chemistry was determined by sampling pore water from ... -
Effects of H2S and CO2 on Cement/Casing interface corrosion integrity for cold climate oil and gas well applications
(The Electrochemical Society, 2016)Low-temperature corrosion relevant to oil and gas wells was investigated. Casing cement was exposed to brine in contact with CO2 at 4 °C and 10 MPa. Pore water was extracted from wet cement using a die press, and a cement ... -
Electrochemical corrosion behavior of high strength carbon steel in H2S-Containing alkaline brines
(The Electrochemical Society, 2015)The electrochemical corrosion behavior of high strength low alloy carbon steel API S-135 was investigated using in-situ electrochemical measurements, ex situ surface analyses, and software modeling in the alkaline brines ...