Corrosion behavior of ultra-high strength drilling steel in alkaline brines containing hydrogen sulfide at high temperature
(Nace International, 2016)
In-situ electrochemical measurements were used to study the sour corrosion of ultra-high strength low alloy carbon steel (UHSLA) in alkaline brines at 200 °C. The solutions were buffered with NaHCO3 / Na2CO3 / NaOH to pH ...
Effects of CO2 and H2S on corrosion of martensitic steels in NaCl(aq) at low temperature
(Nace International, 2016)
Corrosion studies were conducted for martensitic carbon steels in brine solutions at 4 °C and 10 MPa (1450 psi), which simulated the subsurface environments encountered in Arctic drilling. Three environments with a 5 % wt. ...
The coating of hydroxyapatite ( HAP ) on 316L stainless steel and Ti6Al4V alloy use by Sol-Gel method
(Afyon Kocatepe Üniversitesi, 2010)
In this research, hydroxyapatite (HAP) coatings have been coated on Ti6Al4V alloy and 316 L stainless steel substrates by sol-jel method. (NH4)H2PO4 is taken as P precursor and Ca(NO3)2.4H2O is taken as Ca precursor to ...
Corrosion behavior of 13Cr casing steel in cement-synthetic pore solution exposed to high pressure CO2 and H2S
(The Electrochemical Society, 2015)
As deeper wells drilled for oil and gas extraction encounter higher pressures, temperatures, and concentrations in the downhole environment, it becomes increasingly important to consider the integrity of the casing that ...
Effect of H2S and CO2 on Cement/Casing alloy interface corrosion integrity for cold climate oil and gas well applications
(The Electrochemical Society, 2016)
A study has been carried out to investigate sweet and sour corrosion at the cement-casing interface for offshore oil and gaswells in cold climate. The test solution chemistry was determined by sampling pore water from ...
Corrosion of 13Cr steel at the Cement/Casing interface in CO2/H2S environments at 4, 85 and 200 °C
(Nace International, 2018)
A study was carried out to investigate corrosion at the cement/casing interface for 13Cr casing steel. Cement simulated pore solution (CSPS) was developed by exposing cement pieces to 5% NaCl at 100 °C and 10 MPa in ...
Investigation of corrosion behaviors at different solutions of boronized AISI 316L stainless steel
(Springer, May 2013)
In this study, corrosion behaviors of boronized and non-boronized AISI 316L stainless steel (AISI 316L SS) were investigated with Tafel extrapolation and linear polarization methods in different solutions (1 mol dm−3 HCl, ...
Corrosion and wear behaviors of boronized AISI 316L stainless steel
(Springer, 2013)
In this study, the effects of a boronizing treatment on the corrosion and wear behaviors of AISI 316L austenitic stainless steel (AISI 316L) were examined. The corrosion behavior of the boronized samples was studied via ...
Corrosion inhibition of st37 steel in geothermal fluid by quercus robur and pomegranate peels extracts
(Pleiades Publishing, Ltd, 2015)
Plant extracts have become important as an environmentally acceptable, readily available and renewable source of wide range of inhibitors. Tannins, a class of natural, non toxic and biodegradable polyphenolic compounds, ...
The effect of polypyrrole and nickel + polypyrrole coatings on corrosion behaviour AISI 304 stainless steel
(Pleiades Publishing, Ltd, 2015)
Polypyrrole (PPy) and nickel + PPy (Ni + PPy) coatings have been occured on AISI 304 stainless steel (304 SS) surface by cyclic voltammetry technique in aqueous oxalic acid solutions and as the supporting electrolytes was ...