Corrosion behavior of 13Cr casing steel in cement-synthetic pore solution exposed to high pressure CO2 and H2S
(The Electrochemical Society, 2015)
The electrochemical corrosion behavior of grade L-80, type 13Cr casing steel was investigated in cement-synthetic pore solution (CSPS) exposed to CO2 and H2S using in-situ electrochemical methods and ex-situ surface analyses ...
Effects of CO2 and H2S on corrosion of martensitic steels in brines at low temperature
(Nace International, 2018)
Corrosion studies were conducted for martensitic carbon steels in 5 wt% NaCl brine solutions at 4°C and 10 MPa (1,450 psi). These studies simulated different subsurface environments relevant to Arctic drilling. Here, two ...
Effects of H2S and CO2 on Cement/Casing interface corrosion integrity for cold climate oil and gas well applications
(The Electrochemical Society, 2016)
Low-temperature corrosion relevant to oil and gas wells was investigated. Casing cement was exposed to brine in contact with CO2 at 4 °C and 10 MPa. Pore water was extracted from wet cement using a die press, and a cement ...